Energy dissipation at the silica glass/compressed aerogel interface: The fate of Wild 2 mineral grains and fragments smaller than ~100 nm

1Frans J. M. Rietmeijer
Meteoritics & Planetary Science (in Press) Link to Article [DOI: 10.1111/maps.12695]
1Department of Earth and Planetary Sciences, MSC03-2040, University of New Mexico, Albuquerque, New Mexico, USA
Published by arrangement with John Wiley & Sons

Allocation FC6,0,10,0,26 from Stardust track 10 shows a slightly wavy silica glass/compressed silica aerogel interface exposing a patchwork of compressed silica aerogel domains and domains of silica glass with embedded Wild 2 materials in ultra-thin TEM sections. This interface is where molten silica encountered compressed silica aerogel at temperatures <100 °C, and probably near room temperature, causing steep thermal gradients. An Mg, Fe-olivine grain, and a plagioclase-leucite intergrowth survived without melting in silica glass. A Mg-, Al-, Ca-, K-bearing silica globule moved independently as a single object. Two clusters of pure iron, low-Ni iron, and low-Ni, low-sulfur Fe-Ni-S grains also survived intact and came to rest right at the interface between silica glass/compressed silica aerogel. There are numerous Fe-Ni-S nanograins scattered throughout MgO-rich magnesiosilica glass, but compositionally similar Fe-Ni-S are also found in the compressed silica aerogel, where they are not supposed to be. This work could not establish how deep they had penetrated the aerogel. Iron nanograins in this allocation form core-ring grains with a gap between the iron core and a surrounding ring of thermally modified aerogel. This structure was caused when rapid, thermal expansion of the core heated the surrounding compressed aerogel that upon rapid cooling remained fixed in place while the iron core shrank back to its original size. The well-known volume expansion of pure iron allowed reconstruction of the quench temperature for individual core-ring grains. These temperatures showed the small scale of thermal energy loss at the silica glass/compressed silica aerogel interface. The data support fragmentation of olivine, plagioclase, and iron and Fe ± low-Ni grains from comet 81P/Wild 2 during hypervelocity capture.

Discuss

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out /  Change )

Google+ photo

You are commenting using your Google+ account. Log Out /  Change )

Twitter picture

You are commenting using your Twitter account. Log Out /  Change )

Facebook photo

You are commenting using your Facebook account. Log Out /  Change )

Connecting to %s